Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS K/30 LATI ITALY
LATILUB
--
Filler: Carbon fiber rein、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/LATI ITALY/K/30
Shrinkage rate
TD:2.00mm
ISO294-4
%
0
Shrinkage rate
MD:2.00mm
ISO294-4
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/LATI ITALY/K/30
Tensile modulus
23°C
ISO527-2/1
Mpa
2
Tensile modulus
60°C
ISO527-2/1
Mpa
2
Tensile modulus
90°C
ISO527-2/1
Mpa
2
Tensile modulus
120°C
ISO527-2/1
Mpa
1
Tensile modulus
150°C
ISO527-2/1
Mpa
1
Tensile strain
断裂,23°C
ISO527-2/5
%
0
Tensile strain
断裂,60°C
ISO527-2/5
%
0
Tensile strain
断裂,90°C
ISO527-2/5
%
1
Tensile strain
断裂,120°C
ISO527-2/5
%
1
Tensile strain
断裂,150°C
ISO527-2/5
%
1
Tensile stress
断裂,23°C
ISO527-2/5
Mpa
1
Tensile stress
断裂,60°C
ISO527-2/5
Mpa
1
Tensile stress
断裂,90°C
ISO527-2/5
Mpa
1
Tensile stress
断裂,120°C
ISO527-2/5
Mpa
8
Tensile stress
断裂,150°C
ISO527-2/5
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PPS/LATI ITALY/K/30
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Vicat softening temperature
ISO306/B50
°C
2
Linear coefficient of thermal expansion
MD：30到100°C
ISO11359-2
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PPS/LATI ITALY/K/30
Surface resistivity
ASTMD257
ohms
1
Volume resistivity
ASTMD257
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPS/LATI ITALY/K/30
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
2