Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PX9406P 基础创新塑料(南沙)
--
电子通讯配件、电子通讯配件、建筑材料、型材
阻燃
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Thermal Properties
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Deflection Temperature Under Load?
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Deflection Temperature Under Load?
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 5
ISO 75-2/Af
°C
1
Ball PressureTest
125°C
IEC 60695-10-2
通
Linear thermal expansion coefficient
流动 : -30 到 30°C
TMA
cm/cm/°C
7
Linear thermal expansion coefficient
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
6
Deflection Temperature Under Load?
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Linear thermal expansion coefficient
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Vicat Softening Temperature
--
ISO 306/A120
°C
1
Vicat Softening Temperature
--
ISO 306/B120
°C
1
Fill Analysis
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Melt Viscosity
280°C, 1500 sec^-1
ISO 11443
Pa·s
2
Injection
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Middle Temperature
°C
2
Drying Time
hr
3
Suggested Shot Size
%
3
Drying Temperature
°C
1
Mold Temperature
°C
7
Vent Depth
mm
0
Suggested Max Moisture
%
0
Processing (Melt) Temp
°C
2
Rear Temperature
°C
2
Nozzle Temperature
°C
2
Front Temperature
°C
2
Back Pressure
Mpa
0
Screw Speed
rpm
2
Physical
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Melt Mass-Flow Rate
250°C/10.0 kg
ASTM D1238
g/10 min
3
Melt Volume flow Rate
280°C/10.0 kg
ISO 1133
cm3/10min
2
Melt Volume flow Rate
280°C/5.0 kg
ISO 1133
cm3/10min
1
Moisture Absorption
24 hr
ASTM D570
%
0
Modeling Shrinkage - Flow
3.20 mm
内部方法
%
0
Melt Volume flow Rate
300°C/5.0 kg
ISO 1133
cm3/10min
2
Mechanical Properties
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Tensile Stress
屈服
内部方法
Mpa
6
Flexural Modulus
--
ASTM D790
Mpa
2
Flexural Modulus
-- 2
ISO 178
Mpa
2
Flexural Strength
--
ASTM D790
Mpa
9
Flexural Strength
-- 2, 3
ISO 178
Mpa
1
Tensile Strain
断裂
内部方法
%
8
Tensile Strain
断裂
ISO 527-2/50
%
4
Tensile Stress
屈服
ISO 527-2/50
Mpa
7
Impact Properties
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Charpy Unnotched Impact Strength
-30°C
ISO 179/1eU
kJ/m²
9
Flammability
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
UL flame retardant rating
0.75 mm
UL 94
V
UL flame retardant rating
0.40 mm
UL 94
V
UL flame retardant rating
2.5 mm
UL 94
5
Electrical Properties
Test Condition
Test Method
Unit
PPO/基础创新塑料(南沙)/PX9406P
Dielectric Constant
60 Hz
ASTM D150
2
Dielectric Constant
50 kHz
ASTM D150
2
Surface Resistivity
ASTM D257
ohms
1