Density/specific gravity

ASTMD792

g/cm³

1

Density/specific gravity

ISO1183

g/cm³

1

Melt mass flow rate

190°C/2.16kg

ASTMD1238

g/10min

9

Melt mass flow rate

190°C/2.16kg

ISO1133

g/10min

9

Shrinkage rate

MD

ASTMD955

%

1

Shrinkage rate

TD

ISO294-4

%

2

Shrinkage rate

MD

ISO294-4

%

2

Water absorption rate

23°C,24hr

ISO62

%

0

Water absorption rate

平衡,23°C,60%RH

ASTMD570

%

0

Tensile strength

屈服,23°C

ASTMD638

Mpa

4

Tensile strain

断裂,23°C

ISO527-2

%

>

Tensile stress

屈服,23°C

ISO527-2

Mpa

4

elongation

屈服,23°C

ASTMD638

%

8

Bending modulus

23°C

ASTMD790

Mpa

1

Bending modulus

23°C

ISO178

Mpa

1

bending strength

23°C

ASTMD790

Mpa

6

Bending stress

23°C

ISO178

Mpa

5

Hot deformation temperature

0.45MPa,未退火

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,未退火

ASTMD648

°C

8

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

8

Melting temperature

ISO11357-3

°C

1

Linear coefficient of thermal expansion

MD

ASTMD696

cm/cm/°C

1

Surface resistivity

ASTMD257

ohms

1

Surface resistivity

IEC60093

ohms

1

Dielectric strength

ASTMD149

KV/mm

1

Dielectric strength

IEC60243-1

KV/mm

1

Volume resistivity

IEC60093

ohms·cm

1

Volume resistivity

ASTMD257

ohms·cm

1

Charpy Notched Impact Strength

23°C

ISO179/1eA

kJ/m²

1

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

1