ABS PA-718 TAIWAN CHIMEI
POLYLAC®
Electrical field、Electronic field、small home appliances
High impact resistance、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-718
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-718
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
tensile elongation
1/8＂ 6mm/min
ASTM D-638
%
3
elongation
ASTM D638/ISO 527
%
3
Flexural elasticity
1/4＂ 2.8mm/min
ASTM D-790
kg/cm2(lb/in2)
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
7
bending strength
1/4＂ 2.8mm/min
ASTM D-790
kg/cm2(lb/in2)
7
Tensile strength
1/8＂ 6mm/min
ASTM D-638
kg/cm2(lb/in2)
4
hardness
1/2＂
ASTM D-785
R scale
1
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
IZOD impact strength
1/4＂ 23℃
ASTM D-256
kg·cm/cm(ft-lb/in)
1
IZOD impact strength
1/8 ＂23℃
ASTM D-256
kg·cm/cm(ft-lb/in)
1
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-718
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
9
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
8
Hot deformation temperature
1/4＂，120℃/hr
ASTM D-648
℃（℉）
9
Hot deformation temperature
1/4＂，120℃/hr
ASTM D-648
℃（℉）
8
softening point
1/8＂，50℃/hr
ASTM D-1525
℃（℉）
1
vicat softening point
ASTM D1525/ISO R306
℃（℉）
1