PC/ABS CX7240-111 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electrical field、Electronic field、Electronic display、Engine hood parts、Aerospace Applications、Nursing supplies、Architectural application、Outdoor applications、Liquid handling、Medical supplies、Lighting fixtures
Flame retardant、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-111
Melt flow rate
260°C/2.16 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
260°C/2.16 kg
ISO 1133
cm3/10min
1
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-111
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
4
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 3
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
9
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending stress
-- 5, 6
ISO 178
Mpa
9
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-111
RTI
UL 746
°C
9
RTI Elec
UL 746
°C
9
RTI Imp
UL 746
°C
9
thermal conductivity
ISO 8302
W/m/K
0
Vicat softening temperature
--
ASTM D152511, ISO 306/B5011
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831, ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
9
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
ISO 75-2/Af
°C
9
Electrical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-111
Surface resistivity
IEC 60093
ohms
>
Dielectric strength
0.800 mm, 在油中
IEC 60243-1
KV/mm
3
Dielectric strength
1.60 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Volume resistivity
IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-111
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
6
flammability
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-111
Extreme Oxygen Index
ISO 4589-2
%
3
Hot filament ignition temperature
0.75 mm 13
IEC 60695-2-13
°C
7
Hot filament ignition temperature
1.0 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
1.5 mm 13
IEC 60695-2-13
°C
7
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
3.0 mm 13
IEC 60695-2-13
°C
7
Burning wire flammability index
0.75 mm
IEC 60695-2-12
°C
9
Burning wire flammability index
0.75 mm 13
IEC 60695-2-12
°C
9