Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RF005 BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical、Chemical equipment、mechanical、sporting goods
Thermal stability、High temperature resistan、Filler: Glass fiber reinf、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF005 BK
Shrinkage rate
MD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ASTMD955
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF005 BK
Tensile strength
断裂
ASTMD638
Mpa
1
Tensile strength
断裂
ISO527-2
Mpa
1
Tensile modulus
--2
ASTMD638
Mpa
9
Tensile modulus
--
ISO527-2/1
Mpa
8
elongation
断裂
ASTMD638
%
1
elongation
断裂
ISO527-2
%
2
Bending modulus
--
ASTMD790
Mpa
7
Bending modulus
--
ISO178
Mpa
8
bending strength
--
ASTMD790
Mpa
1
bending strength
--
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF005 BK
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距4
ISO75-2/Af
°C
2
Impact performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF005 BK
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
4
Cantilever beam without notch impact strength
23°C3
ISO180/1U
kJ/m²
3
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
7
Dart impact equipped with measuring instruments
--
ISO6603-2
J
2