Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PX9406P-701 SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Electronic communication 、Electronic communication 、building materials、Profile
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PX9406P-701
Melt flow rate
250°C/10.0 kg
ASTM D1238
g/10 min
3
Molten Volume Flow Rate (MVR)
280°C/10.0 kg
ISO 1133
cm3/10min
2
Molten Volume Flow Rate (MVR)
280°C/5.0 kg
ISO 1133
cm3/10min
1
Molten Volume Flow Rate (MVR)
300°C/5.0 kg
ISO 1133
cm3/10min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PX9406P-701
Tensile strain
断裂
内部方法
%
8
Tensile strain
断裂
ISO 527-2/50
%
4
Tensile stress
屈服
内部方法
Mpa
6
Tensile stress
屈服
ISO 527-2/50
Mpa
7
Bending modulus
--
ASTM D790
Mpa
2
Bending modulus
-- 2
ISO 178
Mpa
2
bending strength
--
ASTM D790
Mpa
9
bending strength
-- 2, 3
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PX9406P-701
Vicat softening temperature
--
ISO 306/A120
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -30 到 30°C
TMA
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 5
ISO 75-2/Af
°C
1
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PX9406P-701
Surface resistivity
ASTM D257
ohms
1
Filling analysis
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PX9406P-701
Melt viscosity
280°C, 1500 sec^-1
ISO 11443
Pa·s
2
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PX9406P-701
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
kJ/m²
9