Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 8035 000000 COVESTRO SHANGHAI
Makrolon®
Electrical field、Electronic field、Fiber grade
High temperature resistan、enhance、Filler: Glass fiber with 、30%、Filler by weight、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
Apparent density 2
ISO60
g/cm³
0
Density/specific gravity
23°C
ISO1183
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
4
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
5
Shrinkage rate
TD
ISO2577
%
0
Shrinkage rate
MD
ISO2577
%
0
Shrinkage rate
TD:2.00mm3
ISO294-4
%
0
Shrinkage rate
MD:2.00mm3
ISO294-4
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
TensileCreepModule
1hr
ISO899-1
Mpa
4
Tensile modulus
23°C
ISO527-2/1
Mpa
5
Tensile creep modulus
1000hr
ISO899-1
Mpa
3
Tensile strain
屈服,23°C
ISO527-2/50
%
2
Tensile strain
断裂,23°C
ISO527-2/5
%
3
Tensile stress
断裂,23°C
ISO527-2/5
Mpa
5
Tensile stress
屈服,23°C
ISO527-2/50
Mpa
5
Bending modulus 4
23°C
ISO178
Mpa
4
Bending strain 5
23°C
ISO178
%
4
Bending stress 4
3.5%Strain,23°C
ISO178
Mpa
1
Bending stress 4
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
RTIElec
1.5mm
UL746
°C
1
Evolution Calendar intelligent importer
1.5mm
UL746
°C
1
RTIStr
1.5mm
UL746
°C
1
Thermal conductivity coefficient 8
23°C
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：23to55°C
ISO11359-2
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
Surface resistivity
IEC60093
ohms
1
Dielectric strength
23°C,1.00mm
IEC60243-1
KV/mm
3
Leakage Trace Index
解决方案A
IEC60112
V
1
Leakage Trace Index
解决方案B
IEC60112
V
1
Volume resistivity
23°C
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
CharpyNotchedImpactStrength6
23°C,CompleteBreak
ISO7391
kJ/m²
8
NotchedIzodImpactStrength7
23°C,CompleteBreak
ISO7391
kJ/m²
8
Multi axis Instrumented Peak Impact Force
-30°C
ISO6603-2
N
8
Multi axis Instrumented Peak Impact Force
23°C
ISO6603-2
N
1
Multi axis Instrumented Impact Energy
-30°C
ISO6603-2
J
5
Multi axis Instrumented Impact Energy
23°C
ISO6603-2
J
5
Impact strength of simply supported beam without notch
-60°C,CompleteBreak
ISO179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
-30°C,完全断裂
ISO179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
23°C,完全断裂
ISO179/1eU
kJ/m²
4
hardness
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
Ball pressure hardness
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PC/COVESTRO SHANGHAI/8035 000000
FlashIgnitionTemperature
ASTMD1929
°C
4
SelfIgnition
ASTMD1929
°C
5
Extreme Oxygen Index 9
ISO4589-2
%
3
Hot filament ignition temperature
1.5mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
0.75mm
IEC60695-2-13
°C
8
Needle flame test
MethodF:1.50mm
IEC60695-11-5
min
2
Needle flame test
MethodF:2.00mm
IEC60695-11-5
min
2
Needle flame test
MethodF:3.00mm
IEC60695-11-5
min
2
Needle flame test
MethodK:1.50mm
IEC60695-11-5
min
1
Needle flame test
MethodK:2.00mm
IEC60695-11-5
min
1
Needle flame test
MethodK:3.00mm
IEC60695-11-5
min
2
Burning wire flammability index
0.75mm
IEC60695-2-12
°C
9
Burning wire flammability index
1.5mm
IEC60695-2-12
°C
9
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
9