Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5201-X10-BK TORAY JAPAN
Toraycon®
Electrical field、Electronic field、Automotive sector
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5201-X10-BK
Shrinkage rate
TD:3.00mm2
内部方法
%
2
Shrinkage rate
MD:3.00mm4
内部方法
%
2
Water absorption rate
23°C,24hr
ISO62
%
0
Water absorption rate
23℃·24小时
ASTM D-570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5201-X10-BK
IZOD impact strength (1/8 hour width)
无缺口，23℃
ASTM D-256
kg.cm/cm
不
IZOD impact strength (1/8 hour width)
无缺口，-40℃
ASTM D-256
kg.cm/cm
1
IZOD impact strength (1/8 hour width)
缺口，23℃
ASTM D-256
kg.cm/cm
6
IZOD impact strength (1/8 hour width)
缺口，-40℃
ASTM D-256
kg.cm/cm
5
Fracture tensile elongation
23℃
ASTM D-638
%
>
Under load
4.6kg/cm
ASTM D-648
°C
1
Under load
18.6kg.cm
ASTM D-648
°C
5
Tensile modulus
23°C
ISO527-2
Mpa
2
tensile strength
23℃
ASTM D-638
kg/cm
4
Tensile strain
断裂,23°C
ISO527-2
%
5
Tensile stress
屈服,23°C
ISO527-2
Mpa
5
Rockwell hardness
23℃
ASTM D-785
M标度
5
Bending modulus
23°C
ISO178
Mpa
2
Bending modulus
23℃
ASTM D-790
kg/cm
2
bending strength
23℃
ASTM D-790
kg/cm
7
Bending stress
23°C
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5201-X10-BK
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
5
Linear coefficient of thermal expansion
MD：-30到100°C
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5201-X10-BK
Dielectric strength
IEC60243-1
KV/mm
1
Arc resistance 5
IEC60950
sec
1
Volume resistivity
IEC60093
ohms·cm
4
Impact performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5201-X10-BK
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
2
Supplementary Information
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5201-X10-BK
BarFlowLength6
250°C,1.00mm
内部方法
CM
8