Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/MXD6 1524-9008 SOLVAY USA
IXEF®
Phone、Shell
Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA/MXD6/SOLVAY USA/1524-9008
Shrinkage rate
MD
内部方法
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Water absorption rate
平衡,50%RH
内部方法
%
1
Water absorption rate
Equilibrium,65%RH
内部方法
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA/MXD6/SOLVAY USA/1524-9008
Tensile modulus
ISO527-2
Mpa
2
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
屈服
ISO527-2
Mpa
2
Bending modulus
ISO178
Mpa
1
Bending stress
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA/MXD6/SOLVAY USA/1524-9008
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA/MXD6/SOLVAY USA/1524-9008
Leakage Trace Index
IEC60112
V
>
Hot wire ignition (HWI)
0.400mm
UL746
sec
9
Hot wire ignition (HWI)
0.750mm
UL746
sec
>
Hot wire ignition (HWI)
1.50mm
UL746
sec
>
Hot wire ignition (HWI)
3.00mm
UL746
sec
>
Compared to the anti leakage trace index
3.00mm
UL746
V
>
Impact performance
Test Condition
Test Method
Unit
PA/MXD6/SOLVAY USA/1524-9008
Impact strength of simply supported beam without notch
ISO179/1eU
kJ/m²
4
flammability
Test Condition
Test Method
Unit
PA/MXD6/SOLVAY USA/1524-9008
Extreme Oxygen Index
ISO4589-2
%
3
Hot filament ignition temperature
0.40mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
0.75mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
1.5mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8