Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 3300HR CELANESE USA
CELANEX®
Automotive sector
Glass fiber reinforced、Hydrolysis stability leve
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/CELANESE USA/3300HR
Density/specific gravity
ISO 1183
kg/m
1
Shrinkage rate
纵向
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/3300HR
IZOD notch impact strength
23℃
ISO 180/1A
KJ/m
1
IZOD notch free impact strength
23℃
ISO 180/1U
KJ/m
3
elongation at break
5mm/min
ISO 527-2/1A
%
2
Charpy Notched Impact Strength
23℃
ISO 179/1eA
KJ/m
8
Charpy Notched Impact Strength
-30℃
ISO 179/1eA
KJ/m
8
Impact strength of simply supported beam without notch
23℃
ISO 179/1eU
KJ/m
4
Impact strength of simply supported beam without notch
-30℃
ISO 179/1eU
KJ/m
4
Tensile modulus
1mm/min
ISO 527-2/1A
Mpa
9
tensile strength
5mm/min
ISO 527-2/1A
Mpa
1
Bending modulus
23℃
ISO 178
Mpa
9
bending strength
23℃
ISO 178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/3300HR
Glass transition temperature
ISO 11357-1,-2,-3
°C
6
Hot deformation temperature
1.8Mpa
ISO 75-1/-2
°C
2
Hot deformation temperature
0.45Mpa
ISO 75-1/-2
°C
2
Melting temperature
ISO 11357-1,-2,-3
°C
2
Vicat softening temperature
ISO 306
°C
2
Coefficient of linear expansion
纵向
ISO 11359-2
E-4/℃
0
Coefficient of linear expansion
横向
ISO 11359-2
E-4/℃
1
Electrical performance
Test Condition
Test Method
Unit
PBT/CELANESE USA/3300HR
Surface resistivity
IEC 60093
Ohm
＞
Dielectric strength
IEC 60243-1
KV/mm
3
Dielectric dissipation factor
100Hz
IEC 60250
E-4
2
Dielectric dissipation factor
1MHz
IEC 60250
E-4
1
Volume resistivity
IE 60093
ohm.m
＞