Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3001G-45 TORAY JAPAN
Amilan®
OA device、electrical equipment
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3001G-45
density
23°C
ISO 1183
g/cm³
1
Shrinkage rate 3
横向流量 : 3.00 mm
内部方法
%
0
Shrinkage rate 3
流量 : 3.00 mm
内部方法
%
0
Water absorption rate
24 hr, 23°C
ISO 62
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
5
Mechanical performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3001G-45
shear strength
23°C
ASTM D732
Mpa
9
Tensile strain
断裂, -40°C
ISO 527-2
%
2
Tensile strain
断裂, 23°C
ISO 527-2
%
2
Tensile strain
断裂, 80°C
ISO 527-2
%
5
Tensile stress
-40°C
ISO 527-2
Mpa
2
Tensile stress
23°C
ISO 527-2
Mpa
1
Tensile stress
80°C
ISO 527-2
Mpa
1
Taber abraser
1000 Cycles
ISO 9352
mg
0
Bending modulus
-40°C
ISO 178
Mpa
1
Bending modulus
23°C
ISO 178
Mpa
9
Bending modulus
80°C
ISO 178
Mpa
5
Bending stress
-40°C
ISO 178
Mpa
3
Bending stress
23°C
ISO 178
Mpa
2
Bending stress
80°C
ISO 178
Mpa
1
Compressive stress
-40°C
ISO 604
Mpa
2
Compressive stress
23°C
ISO 604
Mpa
1
Compressive stress
80°C
ISO 604
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3001G-45
Hot deformation temperature
0.45 MPa, 未退火
ISO 75-2/B
°C
2
Melting temperature
DSC
°C
2
Linear coefficient of thermal expansion - flow
ISO 11359-2
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3001G-45
Dielectric strength
IEC 60243-1
KV/mm
2
Arc resistance 6
UL 746
sec
1
Volume resistivity
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3001G-45
Charpy Notched Impact Strength
-40°C
ISO 179
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO 179
kJ/m²
1
Impact strength of simply supported beam without notch
-40°C
ISO 179
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO 179
kJ/m²
6