Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI AUT195 BK1343M SABIC INNOVATIVE US
ULTEM™
Electrical appliances、Automotive Applications
High mobility、High transparency、high definition
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/AUT195 BK1343M
Melt volume flow rate
340°C/5.0kg
ISO1133
cm3/10min
1
Melt mass flow rate
337°C/6.6kg
ASTMD1238
g/10min
2
Shrinkage rate
TD2
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/AUT195 BK1343M
Flexural Strength4
Yield,100mmSpan
ASTMD790
Mpa
1
Tensile strength 3
屈服
ASTMD638
Mpa
9
Tensile modulus
ISO527-2/1
Mpa
3
Elongation rate 4
断裂
ASTMD638
%
7
Bending modulus 4
100mmSpan
ASTMD790
Mpa
3
Bending modulus 5
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/AUT195 BK1343M
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature 8
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
Hot deformation temperature 8
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Vicat softening temperature
ISO306/B120
°C
2
Linear coefficient of thermal expansion
MD：23到150°C
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：23to150°C
ISO11359-2
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/AUT195 BK1343M
ReverseNotchIzodImpact
3.20mm
ASTMD256
J/m
2
Impact strength of simply supported beam gap 6
23°C
ISO179/1eA
kJ/m²
4
Impact strength of simply supported beam gap 6
-30°C
ISO179/1eA
kJ/m²
4
Suspended wall beam gap impact strength 7
-30°C
ISO180/1A
kJ/m²
5
Suspended wall beam gap impact strength 7
23°C
ISO180/1A
kJ/m²
5
Supplementary Information
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/AUT195 BK1343M
MetallizedHazeOnset
内部方法
°C
1