Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1803R SABIC INNOVATIVE SHANGHAI
SABIC®
Electrical field、Electronic field、Connector、Automotive sector
high viscosity、High temperature resistan、enhance、Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/1803R
Saturation, 23 ° C
ISO62
%
0
Density/specific gravity
ASTMD792,ISO1183
g/cm³
1
Balance, 23 ° C
ASTMD570
%
0
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
1
Shrinkage rate
MD：--1
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/1803R
--
ISO527-2/1
Mpa
2
--2
ASTMD638
Mpa
2
50.0mm span 6
ASTMD790
Mpa
2
--7
ISO178
Mpa
2
--8
ISO178
Mpa
9
crack
ISO527-2/50
%
>
Fracture 5
ASTMD638
%
>
yield
ISO527-2/50
%
6
yield
ISO527-2/50
Mpa
6
Yield, 50.0mm span 9
ASTMD790
Mpa
9
Surrender 3
ASTMD638
Mpa
6
Surrender 4
ASTMD638
%
6
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/1803R
23 to 80 ° C
ISO11359-2
cm/cm/°C
7
-40 to 95 ° C
ASTME831
cm/cm/°C
7
thermal conductivity
DENKA Method
W/m/K
0
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/1803R
Dielectric strength
1.60mm
ASTMD2863
KV/mm
2
Volume resistivity
ASTMD257,IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/1803R
23°C
ASTMD256
J/m
7
23°C11
ISO180/1A
kJ/m²
7
-30°C10
ISO180/1A
kJ/m²
1
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/1803R
transmissivity
2540µm
ASTMD1003
%
8
Haze
2540µm
ASTMD1003
%
<