Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1140-111FC SABIC INNOVATIVE NANSHA
LEXAN™
Safety equipment、packing、Thin walled products、Optical data storage、lens、container
High mobility、Good demolding performanc、Good forming performance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
Melt flow rate
300°C/1.2 kg
ASTM D1238
g/10 min
2
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Specific volume
ASTM D792
cm³/g
0
Water absorption rate
24 hr
ASTM D570
%
0
Water absorption rate
平衡, 23°C
ASTM D570
%
0
Water absorption rate
平衡, 100°C
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
6
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
6
elongation
屈服
ISO 527-2/50
%
6
elongation
断裂 3
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
7
Taber abraser
1000 Cycles, 1000 g, CS-17 转轮
ASTM D1044
mg
1
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending stress
-- 5, 6
ISO 178
Mpa
9
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
specific heat
ASTM C351
J/kg/°C
1
thermal conductivity
--
ASTM C177
W/m/K
0
thermal conductivity
--
ISO 8302
W/m/K
0
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion - flow
-40 到 95°C
ASTM E831
cm/cm/°C
6
Linear coefficient of thermal expansion - flow
23 到 80°C
ISO 11359-2
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11
ISO 75-2/Be
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11
ISO 75-2/Ae
°C
1
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
Surface resistivity
IEC 60093
ohms
>
Dielectric strength
3.20 mm, in Air
ASTM D149
KV/mm
1
Dielectric strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Volume resistivity
--
ASTM D257
ohms·cm
>
Volume resistivity
--
IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
Impact strength of simply supported beam gap 7
-30°C
ISO 179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 7
23°C
ISO 179/1eA
kJ/m²
1
Tensile impact strength 10
ASTM D1822
kJ/m²
3
Falling hammer impact
23°C
ASTM D3029
J
1
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
3
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
5
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
Extreme Oxygen Index
ISO 4589-2
%
2
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/HF1140-111FC
transmissivity
2540 µm
ASTM D1003
%
8
Haze
2540 µm
ASTM D1003
%
1