MeltViscosity

200°C,1000sec^-1

ASTMD3835

Pa·s

2

Melt mass flow rate

230°C/3.8kg

ASTMD1238

g/10min

4

Melt mass flow rate

220°C/5.0kg

ISO1133

g/10min

1

Shrinkage rate

MD：3.20mm

内部方法

%

0

Tensile strength 3

屈服

ASTMD638

Mpa

4

Tensile strength 3

断裂

ASTMD638

Mpa

3

Tensile modulus 2

ASTMD638

Mpa

2

Tensile strain

屈服

ISO527-2/50

%

2

Tensile strain

断裂

ISO527-2/50

%

3

Tensile stress

断裂

ISO527-2/50

Mpa

3

Tensile stress

屈服

ISO527-2/50

Mpa

4

Elongation rate 3

屈服

ASTMD638

%

2

Elongation rate 4

断裂

ASTMD638

%

9

Bending modulus 4

50.0mm跨距

ASTMD790

Mpa

2

Bending strength 4

屈服,50.0mm跨距

ASTMD790

Mpa

7

RTIElec

UL746

°C

6

Evolution Calendar intelligent importer

UL746

°C

6

RTIStr

UL746

°C

6

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

8

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

7

Hot deformation temperature 7

1.8MPa,未退火,64.0mm跨距

ISO75-2/Af

°C

7

Vicat softening temperature

ASTMD15258

°C

8

Vicat softening temperature

--

ISO306/B50

°C

8

Vicat softening temperature

--

ISO306/B120

°C

8

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

8

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

8

CharpyNotchedImpactStrength5

23°C

ISO179/1eA

kJ/m²

2

Suspended wall beam notch impact strength 6

-30°C

ISO180/1A

kJ/m²

6

Suspended wall beam notch impact strength 6

23°C

ISO180/1A

kJ/m²

1

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

3