Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE NA207 USI TAIWAN
PAXOTHENE®
film
Lubricity、High mobility、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
LDPE/USI TAIWAN/NA207
density
ASTMD792
g/cm³
1
density
23°C
ISO1183
g/cm³
1
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
200°C/5.0kg
ISO1133
g/10min
2
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
2
Shrinkage rate
MD
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
LDPE/USI TAIWAN/NA207
Tensile strength
23°C
ASTMD638
Mpa
5
Tensile stress
屈服,23°C
ISO527-2
Mpa
5
Bending modulus
23°C
ASTMD790
Mpa
2
Bending modulus
23°C
ISO178
Mpa
2
bending strength
23°C
ASTMD790
Mpa
7
Bending stress
23°C
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
LDPE/USI TAIWAN/NA207
Hot deformation temperature
1.8MPa,Annealed
ISO75-2/A
°C
9
Hot deformation temperature
1.8MPa,未退火,12.7mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,12.7mm
ISO75-2/A
°C
8
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
9
Vicat softening temperature
ISO306/A
°C
1
Vicat softening temperature
ASTMD15254
°C
1
Impact performance
Test Condition
Test Method
Unit
LDPE/USI TAIWAN/NA207
Impact strength of cantilever beam gap
23°C,6.35mm
ISO180
J/m
2
Impact strength of cantilever beam gap
23°C,6.35mm
ASTMD256
J/m
2