PA/MXD6 1035 BLK01 MITSUBISHI ENGINEERING JAPAN
RENY™
--
Filler: Glass fiber reinf、60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1035 BLK01
Melt volume flow rate
275°C/2.16kg
ISO1133
cm3/10min
2
Melt mass flow rate
275°C/2.16kg
ISO1133
g/10min
3
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1035 BLK01
Tensile modulus
ISO527-2
Mpa
2
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending stress
ISO178
Mpa
4
Thermal performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1035 BLK01
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
4
Impact performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1035 BLK01
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
8