Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPU 1190A10 BASF GERMANY
Elastollan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
TPU/BASF GERMANY/1190A10
Melt mass flow rate
190°C/10.0kg
ASTMD1238
g/10min
1
Melt mass flow rate
190°C/21.6kg
ASTMD1238
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
TPU/BASF GERMANY/1190A10
100% tensile stress
ASTM D-412
Mpa
1
300% tensile stress
ASTM D-412
Mpa
1
Abrasion-DIN
DIN53516
mm³
2
Tensile strength at break
ASTM D-412
Mpa
3
Tensile modulus
ASTM D-638
Mpa
3
Tensile modulus
注塑
ASTMD412
Mpa
3
elongation
断裂
ASTM D-412
%
5
tear strength
ASTM D-624
kN/m
1
Taber abraser
ASTMD1044
mg
4
Bending modulus
注塑
ASTMD790
Mpa
2
Bending modulus
ASTM D-790
Mpa
4
Thermal performance
Test Condition
Test Method
Unit
TPU/BASF GERMANY/1190A10
SofteningPoint DMA
内部方法
°C
1
Glass transition temperature
内部方法
°C
-
Vicat softening temperature
ASTMD1525
°C
1
elastomer
Test Condition
Test Method
Unit
TPU/BASF GERMANY/1190A10
Tensile strength
ASTMD412
Mpa
3
Tensile stress
100%应变
ASTMD412
Mpa
1
Tensile stress
300%应变
ASTMD412
Mpa
2
elongation
断裂
ASTMD412
%
4
Tear strength 2
ASTMD624
kN/m
1
Permanent compression deformation
23°C,22hr
ASTMD395B
%
2
Permanent compression deformation
70°C,22hr
ASTMD395B
%
4
Basic performance
Test Condition
Test Method
Unit
TPU/BASF GERMANY/1190A10
density
ASTM D-792
g/cm
1