Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 201-87 CELANESE USA
Santoprene™
Electrical applications、Electrical components、diaphragm、Pipe fittings、Movable hinge、household electrical appl、Home appliance components、Parts under the hood of a、Application in the automo、Automotive Applications、Consumer product applicat
Chemical resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Thermal performance
Test Condition
Test Method
Unit
TPV/CELANESE USA/201-87
RTIElec
UL746
°C
1
RTIStr
1.0mm
UL746
°C
9
RTIStr
1.5mm
UL746
°C
9
RTIStr
3.0mm
UL746
°C
9
Brittle temperature
ASTMD746
°C
-
Brittle temperature
ISO812
°C
-
Electrical performance
Test Condition
Test Method
Unit
TPV/CELANESE USA/201-87
Dielectric strength
23°C,2.00mm
ASTMD149
KV/mm
3
ageing
Test Condition
Test Method
Unit
TPV/CELANESE USA/201-87
ChangeinTensileStrainatBreak
125°C,70hr,inIRM903Oil
ISO1817
%
-
ChangeinTensileStress
125°C,70hr,inIRM903Oil
ISO1817
%
-
ChangeinUltimateElongation
125°C,70hr,inIRM903Oil
ASTMD471
%
-
Change rate of ultimate elongation in air
150°C,168hr
ASTMD573
%
-
Change rate of tensile strength in air
150°C,168hr
ISO188
%
-
Change rate of tensile strength in air
150°C,168hr
ASTMD573
%
-
Change rate of tensile strength
125°C,70hr,inIRM903Oil
ASTMD471
%
-
Volume change
125°C,70hr,在IRM903油中
ASTMD471
%
4
Volume change
125°C,70hr,在IRM903油中
ISO1817
%
4
elastomer
Test Condition
Test Method
Unit
TPV/CELANESE USA/201-87
CompressionSet4
70°C,22hr
ASTMD395B
%
3
CompressionSet4
125°C,70hr
ASTMD395B
%
4
TearStrength-AcrossFlow3
23°C
ISO34-1
kN/m
5
Tensile strength - transverse flow rate
断裂,23°C
ASTMD412
Mpa
1
Tensile strength TD
Break,23°C
ISO37
Mpa
1
Tensile stress transverse flow rate
100%应变,23°C
ASTMD412
Mpa
7
Tensile stress transverse flow rate
100%应变,23°C
ISO37
Mpa
7
Elongation rate - lateral flow rate
断裂,23°C
ASTMD412
%
5
Elongation rate - lateral flow rate
断裂,23°C
ISO37
%
5
Tear strength - transverse flow rate 2
23°C
ASTMD624
kN/m
5
Compression permanent deformation 4
70°C,22hr
ISO815
%
3
Compression permanent deformation 4
125°C,70hr
ISO815
%
4