Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D251RC-701 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D251RC-701
Density/specific gravity
ASTMD792
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
1
Melt volume flow rate
300°C/2.16kg
ISO1133
cm3/10min
2
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Melt mass flow rate
300°C/2.16kg
ASTMD1238
g/10min
3
Shrinkage rate
MD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ASTMD955
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D251RC-701
--
ISO527-2/1
Mpa
6
--1
ASTMD638
Mpa
6
--5
ISO178
Mpa
6
50.0mm span 4
ASTMD790
Mpa
6
--6
ISO178
Mpa
1
crack
ISO527-2/5
Mpa
1
crack
ISO527-2/5
%
2
crack
ISO527-2/5
Mpa
1
Fracture, 50.0mm span 7
ASTMD790
Mpa
1
Fracture 2
ASTMD638
Mpa
1
Fracture 3
ASTMD638
%
2
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D251RC-701
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Linear coefficient of thermal expansion
MD:23到80°C
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD:23到80°C
ISO11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D251RC-701
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
1
Simply supported beam without notch impact strength 9
23°C
ISO179/1eU
kJ/m²
5
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
7
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
2