Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3WG6 BK00564 BASF SHANGHAI
Ultramid®
Engine hood parts、Automotive sector、Application in the automo
Thermal stability、Oil resistant、Filler: Glass fiber reinf、30%、Filler by weight、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/BASF SHANGHAI/B3WG6 BK00564
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
275°C/5.0kg
ISO1133
cm3/10min
4
Water absorption rate
饱和
ASTMD570
%
6
Water absorption rate
饱和,23°C
ISO62
%
6
Water absorption rate
平衡,50%RH
ASTMD570
%
2
Water absorption rate
平衡,23°C,50%RH
ISO62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA6/BASF SHANGHAI/B3WG6 BK00564
Tensile strength
断裂,23°C
ASTMD638
Mpa
1
Tensile modulus
23°C
ISO527-2
Mpa
9
Tensile strain
断裂,23°C
ISO527-2
%
3
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
Bending modulus
23°C
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PA6/BASF SHANGHAI/B3WG6 BK00564
Hot deformation temperature
0.45MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature (DSC)
ISO3146
°C
2
Peak melting temperature
ASTMD3418
°C
2
Impact performance
Test Condition
Test Method
Unit
PA6/BASF SHANGHAI/B3WG6 BK00564
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
9
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
1
Impact strength of simply supported beam without notch
-30°C
ISO179
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
8
Impact strength of cantilever beam gap
-40°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ISO180
kJ/m²
1