Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1414T SABIC INNOVATIVE NANSHA
LEXAN™
Electrical field、Electronic field、Household appliances、Household appliances、Fitness equipment
Low temperature resistanc、transparent、Processability、Moderate liquidity、Ductility、copolymer
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
Density/specific gravity
ASTMD792,ISO1183
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
Tensile strength
屈服4
ASTMD638
Mpa
5
Tensile strength
屈服
ISO527-2/50
Mpa
5
Tensile strength
断裂4
ASTMD638
Mpa
5
Tensile strength
断裂
ISO527-2/50
Mpa
5
Tensile modulus
--3
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1
Mpa
2
elongation
屈服4
ASTMD638
%
5
elongation
屈服
ISO527-2/50
%
5
elongation
断裂4
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
1
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
2
Bending stress
--6,7
ISO178
Mpa
8
Bending stress
屈服,50.0mm跨距5
ASTMD790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
RTI
UL746
°C
1
RTIElec
UL746
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距10
ISO75-2/Af
°C
1
Vicat softening temperature
--
ASTMD152511,ISO306/B12011
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD:-40到95°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
MD:23到80°C
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD:-40到95°C
ASTME831
cm/cm/°C
8
Linear coefficient of thermal expansion
TD:23到80°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
Surface resistivity
ASTMD257
ohms
>
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
7
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
7
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
8
Impact strength of cantilever beam gap
-30°C9
ISO180/1A
kJ/m²
5
Impact strength of cantilever beam gap
23°C9
ISO180/1A
kJ/m²
6
Dart impact equipped with measuring instruments
-30°C,TotalEnergy
ASTMD3763
J
7
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
7
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
Hot filament ignition temperature
0.8mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
9
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414T
transmissivity
2540µm
ASTMD1003
%
8
Haze
2540µm
ASTMD1003
%
3