Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC RX2530 451118 COVESTRO THAILAND
Makrolon®
electrical equipment、Automotive Applications、Lighting installation
Flame retardant、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
Apparent density
ISO60
g/cm³
0
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
1
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
1
Shrinkage rate
TD
ISO2577
%
0
Shrinkage rate
MD
ISO2577
%
0
Shrinkage rate
TD:2.00mm3
ISO294-4
%
0
Shrinkage rate
MD:2.00mm3
ISO294-4
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
Nominal tensile fracture strain
23°C
ISO527-2/50
%
>
Tensile modulus
23°C
ISO527-2/1
Mpa
2
Tensile strain
屈服,23°C
ISO527-2/50
%
6
Tensile strain
断裂,23°C
ISO527-2/50
%
1
Tensile stress
屈服,23°C
ISO527-2/50
Mpa
6
Tensile stress
断裂,23°C
ISO527-2/50
Mpa
7
Bending modulus 4
23°C
ISO178
Mpa
2
Bending strain 5
23°C
ISO178
%
7
Bending stress 4
3.5%Strain,23°C
ISO178
Mpa
7
Bending stress 4
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
Glass transition temperature 8
ISO11357-2
°C
1
Thermal conductivity coefficient 9
23°C
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：23to55°C
ISO11359-2
cm/cm/°C
6
Electrical performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
Surface resistivity
IEC60093
ohms
1
Volume resistivity
23°C
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
Multi axis Instrumented Peak Impact Force
-30°C
ISO6603-2
N
6
Multi axis Instrumented Peak Impact Force
23°C
ISO6603-2
N
5
Multi axis Instrumented Impact Energy
-30°C
ISO6603-2
J
7
Multi axis Instrumented Impact Energy
23°C
ISO6603-2
J
6
Impact strength of simply supported beam gap 6
-30°C,完全断裂
ISO7391
kJ/m²
1
Impact strength of simply supported beam gap 6
23°C,局部断裂
ISO7391
kJ/m²
7
Suspended wall beam gap impact strength 7
-30°C,完全断裂
ISO7391
kJ/m²
1
Suspended wall beam gap impact strength 7
23°C,局部断裂
ISO7391
kJ/m²
6
hardness
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
Ball pressure hardness
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2530 451118
FlashIgnitionTemperature
ASTMD1929
°C
4
SelfIgnition
ASTMD1929
°C
5
Extreme Oxygen Index 10
ISO4589-2
%
2