PPS OCL-4532 LEX BK8115 SABIC INNOVATIVE US
LNP™ STAT-KON™
Automotive Applications
Carbon fiber reinforced、High impact resistance、Filler: Carbon fiber rein
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OCL-4532 LEX BK8115
Shrinkage rate
MD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ISO294-4
%
0
Shrinkage rate
MD:24小时
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OCL-4532 LEX BK8115
Tensile strength
断裂
ASTMD638
Mpa
1
Tensile strength
断裂
ISO527-2
Mpa
1
Tensile modulus
--2
ASTMD638
Mpa
1
Tensile modulus
--
ISO527-2/1
Mpa
1
Wear factor - Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
3
elongation
断裂
ASTMD638
%
1
elongation
断裂
ISO527-2
%
1
Bending modulus
--
ASTMD790
Mpa
9
Bending modulus
--
ISO178
Mpa
9
bending strength
--
ASTMD790
Mpa
1
bending strength
--
ISO178
Mpa
1
Electrical performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OCL-4532 LEX BK8115
Surface resistivity
ASTMD257
ohms
1
Impact performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OCL-4532 LEX BK8115
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
4
Cantilever beam without notch impact strength
23°C3
ISO180/1U
kJ/m²
2
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
8
Dart impact equipped with measuring instruments
--
ISO6603-2
J
2