Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS XR401 9001 LG CHEM KOREA
--
Electronic field、Automotive sector、Automotive interior parts、Automotive External Parts、Shell
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/XR401 9001
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
9
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
9
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
MD：3.20mm
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/XR401 9001
FlexuralStrength3
3.20mm
ASTMD790
Mpa
7
Tensile strength 2
屈服,3.20mm
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/1
Mpa
2
Tensile stress
屈服
ISO527-2/50
Mpa
4
Elongation rate 2
断裂,3.20mm
ASTMD638
%
2
Bending modulus 3
3.20mm
ASTMD790
Mpa
2
Bending modulus 4
ISO178
Mpa
2
Bending stress 4
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/XR401 9001
RTIElec
UL746
°C
6
Evolution Calendar intelligent importer
UL746
°C
6
RTIStr
UL746
°C
6
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature 5
1.8MPa,Unannealed,4.00mm
ISO75-2/Ae
°C
8
Hot deformation temperature 5
0.45MPa,Unannealed,4.00mm
ISO75-2/Be
°C
9
Vicat softening temperature
ASTMD15256
°C
1
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD：23到60°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：23to60°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/XR401 9001
Dielectric strength
23°C,1.00mm
ASTMD149
KV/mm
3
Volume resistivity
23°C
ASTMD257
ohms·cm
1