Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK KT-880 CF30 SOLVAY USA
KETASPIRE®
Electrical field、Electronic field、Industrial applications
Chemical resistance、Fatigue resistance、heat-resisting、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-880 CF30
Density/specific gravity
ASTMD792
g/cm³
1
Melt mass flow rate
400°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate 4
MD:3.18mm
ASTMD955
%
0
Shrinkage rate 4
TD:3.18mm
ASTMD955
%
1
Water absorption rate
24hr
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-880 CF30
shear strength
ASTMD732
Mpa
1
Tensile modulus
--
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1A/1
Mpa
2
Tensile stress
屈服
ISO527-2/1A/5
Mpa
2
Tensile stress
--
ASTMD638
Mpa
2
elongation
断裂5
ASTMD638
%
1
elongation
断裂
ISO527-2/1A/5
%
1
Bending modulus
--
ASTMD790
Mpa
1
Bending modulus
--
ISO178
Mpa
2
bending strength
--
ASTMD790
Mpa
3
bending strength
--
ISO178
Mpa
3
compressive strength
ASTMD695
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-880 CF30
specific heat
50°C
DSC
J/kg/°C
1
specific heat
200°C
DSC
J/kg/°C
1
Glass transition temperature
ASTMD3418
°C
1
thermal conductivity
ASTMC177
W/m/K
0
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
3
Peak melting temperature
ASTMD3418
°C
3
Linear coefficient of thermal expansion
MD：-50到50°C
ASTME831
cm/cm/°C
6
Filling analysis
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-880 CF30
Melt viscosity
400°C,1000sec^-1
ASTMD3835
Pa·s
4
Impact performance
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-880 CF30
Impact strength of cantilever beam gap
--
ISO180
kJ/m²
8
Impact strength of cantilever beam gap
--
ASTMD256
J/m
6
Cantilever beam without notch impact strength
--
ASTMD4812
J/m
6
Cantilever beam without notch impact strength
--
ISO180
kJ/m²
4