Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 13G50 ASAHI JAPAN
Leona™
Electrical applications、Engine parts、Automotive Applications
Fatigue resistance、High rigidity、Creep resistance、high strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G50
Shrinkage rate
横向流量
内部方法
%
0
Shrinkage rate
流量
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
-
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G50
Tensile modulus
23°C
ISO 527-2
Mpa
1
Tensile stress
断裂, 23°C
ISO 527-2
Mpa
2
Tensile stress
--
ASTM D638
Mpa
2
elongation
断裂
ASTM D638
%
2
elongation
断裂, 23°C
ISO 527-2
%
2
Taber abraser
1000 Cycles
ASTM D1044
mg
-
Bending modulus
--
ASTM D790
Mpa
1
Bending modulus
23°C
ISO 178
Mpa
1
bending strength
--
ASTM D790
Mpa
3
bending strength
23°C
ISO 178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G50
Linear coefficient of thermal expansion - flow
ASTM D696
cm/cm/°C
2
Thermal deformation temperature under load
0.45 MPa, 未退火
ASTM D648, ISO 75-2/B
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火
ASTM D648
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火
ISO 75-2/A
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G50
Surface resistivity
ASTM D257, IEC 60093
ohms
1
Dielectric strength
ASTM D149, IEC 60243-1
KV/mm
2
Leakage Trace Index
3.00 mm
IEC 60112
V
5
Volume resistivity
--
ASTM D257
ohms·cm
1
Volume resistivity
23°C
IEC 60093
ohms·cm
1