Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 3412ECR-739 SABIC INNOVATIVE NANSHA
LEXAN™
Electrical appliances、Electronic display、Industrial applications、Automotive External Parts、Medical supplies、Lighting applications
Glass fiber reinforced、enhance、Flame retardant、High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/3412ECR-739
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
7
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
7
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/3412ECR-739
Tensile strength 3
屈服
ASTMD638
Mpa
9
Tensile strength 3
断裂
ASTMD638
Mpa
8
Tensile modulus
ISO527-2/1
Mpa
6
Tensile modulus 2
ASTMD638
Mpa
5
Tensile strain
屈服
ISO527-2/5
%
2
Tensile strain
断裂
ISO527-2/5
%
3
Tensile stress
屈服
ISO527-2/5
Mpa
9
Tensile stress
断裂
ISO527-2/5
Mpa
9
Elongation rate 3
屈服
ASTMD638
%
3
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
5
Bending modulus 5
ISO178
Mpa
5
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,6
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/3412ECR-739
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 9
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Hot deformation temperature 9
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Vicat softening temperature
ASTMD152510
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
3
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/3412ECR-739
Surface resistivity
IEC60093
ohms
>
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/3412ECR-739
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
5
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
6
The impact strength of a simply supported beam without a notch is 7
-30°C
ISO179/1eU
kJ/m²
4
The impact strength of a simply supported beam without a notch is 7
23°C
ISO179/1eU
kJ/m²
4
Unscented Izod Impact Strength 8
-30°C
ISO180/1U
kJ/m²
3
Unscented Izod Impact Strength 8
23°C
ISO180/1U
kJ/m²
3
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
1
Suspended wall beam gap impact strength 8
-30°C
ISO180/1A
kJ/m²
6
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
7
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
2
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/3412ECR-739
Extreme Oxygen Index
ISO4589-2
%
4
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9