Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 53G33 B3378 ASAHI JAPAN
Leona™
Electrical/Electronic App、Engine parts、component、Application in the automo、Automotive Applications、water tank
high strength、High rigidity、Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/53G33 B3378
Shrinkage rate
TD
内部方法
%
0
Shrinkage rate
MD
内部方法
%
0
Shrinkage rate
吸水率(饱和,23°C)
内部方法
%
-
Water absorption rate
平衡,23°C,50%RH
ISO62
%
-
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/53G33 B3378
Tensile strength
ASTMD638
Mpa
2
Tensile modulus
23°C
ISO527-2
Mpa
9
Tensile strain
断裂,23°C
ISO527-2
%
4
Tensile stress
断裂,23°C
ISO527-2
Mpa
2
elongation
断裂
ASTMD638
%
3
Bending modulus
ASTMD790
Mpa
8
Bending modulus
23°C
ISO178
Mpa
9
bending strength
ASTMD790
Mpa
3
Bending stress
23°C
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/53G33 B3378
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear coefficient of thermal expansion
MD
ASTMD696
cm/cm/°C
2
Impact performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/53G33 B3378
Impact strength of simply supported beam without notch
ISO179
kJ/m²
9