Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI DT1810EV-1000 SABIC INNOVATIVE US
ULTEM™
Electrical applications、Automotive Applications
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/DT1810EV-1000
Melt volume flow rate
360°C/5.0kg
ISO1133
cm3/10min
5
Melt mass flow rate
337°C/6.6kg
ASTMD1238
g/10min
4
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/DT1810EV-1000
--
ISO527-2/1
Mpa
2
--1
ASTMD638
Mpa
3
50.0mm span 6
ASTMD790
Mpa
3
--7
ISO178
Mpa
3
--8
ISO178
Mpa
1
crack
ISO527-2/5
%
8
crack
ISO527-2/5
Mpa
8
Fracture 3
ASTMD638
Mpa
8
Fracture 5
ASTMD638
%
8
yield
ISO527-2/5
%
7
yield
ISO527-2/5
Mpa
9
Yield, 50.0mm span 9
ASTMD790
Mpa
1
Surrender 2
ASTMD638
Mpa
1
Surrender 4
ASTMD638
%
7
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/DT1810EV-1000
--
ISO 1183
°C
1
--
ISO306/B120
°C
1
1.8MPa, unannealed, 100mm span 13
ISO75-2/Ae
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 6.40mm
ASTMD648
°C
1
Horizontal: 23 to 150 ° C
ISO11359-2
cm/cm/°C
5
Horizontal: -40 to 150 ° C
ASTME831
cm/cm/°C
6
Flow: 23 to 150 ° C
ISO11359-2
cm/cm/°C
5
Flow: -40 to 150 ° C
ASTME831
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/DT1810EV-1000
23°C
ASTMD256
J/m
3
23°C12
ISO180/1A
kJ/m²
2
-30°C
ASTMD256
J/m
3
-30°C11
ISO180/1A
kJ/m²
2
The impact strength of a simply supported beam with a notch of 10
23°C
ISO179/1eA
kJ/m²
2
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
4