Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1414T-NA8A005T SABIC INNOVATIVE SINGAPHORE
LEXAN™
Electrical applications、Home appliance components、Fitness equipment
Easy to process、Moderate liquidity、Ductility、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Melt flow rate
300°C/1.2 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
9
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
屈服 3
ASTM D638
Mpa
5
Tensile modulus
--
ISO 527-2/1
Mpa
2
Tensile modulus
-- 2
ASTM D638
Mpa
2
elongation
断裂
ISO 527-2/50
%
1
elongation
断裂 3
ASTM D638
%
1
elongation
屈服
ISO 527-2/50
%
5
elongation
屈服 3
ASTM D638
%
5
Bending modulus
-- 5
ISO 178
Mpa
2
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
9
Bending stress
-- 5, 6
ISO 178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
Vicat softening temperature
--
ASTM D152510, ISO 306/B5010
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 95°C
ASTM E831
cm/cm/°C
6
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : -40 到 95°C
ASTM E831
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9
ISO 75-2/Af
°C
1
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Surface resistivity
ASTM D257
ohms
>
Volume resistivity
ASTM D257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Impact strength of simply supported beam gap 7
23°C
ISO 179/1eA
kJ/m²
7
Impact strength of simply supported beam gap 7
-30°C
ISO 179/1eA
kJ/m²
6
Dart impact equipped with measuring instruments
-30°C, Total Energy
ASTM D3763
J
7
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
7
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
Hot filament ignition temperature
0.8 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
8
Burning wire flammability index
3.0 mm
IEC 60695-2-12
°C
9
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SINGAPHORE/EXL1414T-NA8A005T
transmissivity
2540 µm
ASTM D1003
%
8
Haze
2540 µm
ASTM D1003
%
3