Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 1140L4 JAPAN POLYPLASTIC
DURAFIDE®
Fiber grade、Slight flash、During injection molding
Flame retardant、High temperature resistan、enhance、Glass fiber reinforced、Injection grade、Medium melt viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
Density/specific gravity
ASTMD792,ISO1183
g/cm³
1
Mold shrinkage rate
ISO 294-4
%
0
Shrinkage rate
MD
ASTMD955
%
0
Shrinkage rate
TD
ASTMD955
%
0
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
饱和,23°C
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
IZOD notch impact strength
ISO 180/1A
kJ/m²
1
Tensile strength
断裂
ISO527-2/1A/5
Mpa
1
Tensile strength
断裂,23°C
ASTMD638
Mpa
2
Tensile modulus
ISO 527
Mpa
1
Tensile modulus
-40°C
ASTMD638
Mpa
1
Tensile modulus
75°C
ASTMD638
Mpa
1
Tensile modulus
150°C
ASTMD638
Mpa
4
Tensile modulus
200°C
ASTMD638
Mpa
3
Tensile modulus
--
ISO527-2/1A/1
Mpa
1
tensile strength
ISO 527
Mpa
1
Rockwell hardness
ASTM-D785
R-Scale
1
elongation
断裂
ISO527-2/1A/5
%
1
elongation
断裂,23°C
ASTMD638
%
1
Bending modulus
23°C
ISO178
Mpa
1
Bending modulus
ISO 178
Mpa
1
bending strength
ISO 178
Mpa
2
Bending stress 3
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
Glass transition temperature 4
ISO11357-2
°C
9
Hot deformation temperature
0.45MPa,退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
8.0MPa,未退火
ISO75-2/C
°C
2
Hot deformation temperature
1.80Mpa
ISO 75-A
°C
2
Melting temperature 4
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
4
Electrical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
Surface resistivity
IEC60093
ohms
>
Dielectric strength
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
1
Arc resistance
ASTMD495
sec
1
Volume resistivity
--
ASTMD257
ohms·cm
1
Volume resistivity
--
IEC60093
ohms·cm
>
Filling analysis
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
SpecificHeatCapacity of Melt
内部方法
J/kg/°C
1
Impact performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
5
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
5
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
3
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
flammability
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
Extreme Oxygen Index
ISO4589-2
%
4
Basic performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
Density/specific gravity
ISO 1183
g/cm³
1
Water absorption rate
ASTM-D570
%
0
Supplementary Information
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140L4
SpecimensThickness Shrinkage
内部方法
mm
3