Melt mass flow rate

300°C/1.2kg

ISO1133

g/10min

1

Shrinkage rate

MD

ISO294-4

%

0

TensileStrain

Yield,4.00mm,InjectionMolded

ISO527-2/50

%

4

Tensile modulus

4.00mm,InjectionMolded

ISO527-2/1

Mpa

3

Tensile modulus

4.00mm,InjectionMolded

ISO527-2/50

Mpa

4

tensile strength

Yield,4.00mm,InjectionMolded

ISO527-2/50

Mpa

6

Tensile strain

断裂,4.00mm,注塑

ISO527-2/50

%

9

Tensile stress

断裂,4.00mm,注塑

ISO527-2/50

Mpa

5

Bending modulus 2

4.00mm,InjectionMolded

ISO178

Mpa

3

Bending strength 2

4.00mm,InjectionMolded

ISO178

Mpa

1

Ball pressure temperature

IEC60335-1

°C

>

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Hot deformation temperature

1.8MPa,退火

ISO75-2/A

°C

1

Vicat softening temperature

--

ISO306/A120

°C

1

Vicat softening temperature

--

ISO306/B50

°C

1

Linear coefficient of thermal expansion

MD：-40到80°C

ASTMD696

cm/cm/°C

1

Surface resistivity

IEC60093

ohms

1

Dielectric strength

2.00mm

IEC60243-1

KV/mm

>

Volume resistivity

2.00mm

IEC60093

ohms·cm

1

Compared to the anti leakage trace index

3.00mm,SolutionA

IEC60112

V

2

NotchedIzodImpactStrength3

23°C,InjectionMolded

ISO180/A

kJ/m²

9

Extreme Oxygen Index 4

ISO4589-2

%

2

Hot filament ignition temperature 4

1.0mm

IEC60695-2-13

°C

9

Hot filament ignition temperature 4

2.0mm

IEC60695-2-13

°C

9

Hot filament ignition temperature 4

3.0mm

IEC60695-2-13

°C

9