ASTMD792

g/cm³

1

--

ISO1183

g/cm³

1

24hr

ASTMD570

%

0

24hr,50%RH

ASTMD570

%

0

Saturation, 23 ° C

ISO62

%

0

Balance, 23 ° C, 50% RH

ISO62

%

0

Melt volume flow rate

220°C/5.0kg

ISO1133

cm3/10min

1

Melt mass flow rate

260°C/2.16kg

ASTMD1238

g/10min

1

Shrinkage rate

MD:3.20mm

内部方法

%

0

Shrinkage rate

TD:3.20mm

内部方法

%

0

--

ISO527-2/1

Mpa

3

--1

ASTMD638

Mpa

3

50.0mm span 7

ASTMD790

Mpa

3

--8

ISO178

Mpa

3

--9

ISO178

Mpa

9

crack

ISO527-2/50

%

1

crack

ISO527-2/5

Mpa

5

Fracture 4

ASTMD638

Mpa

5

Fracture 6

ASTMD638

%

1

yield

ISO527-2/5

%

3

Yield, 50.0mm span of 10

ASTMD790

Mpa

1

Surrender 2

ASTMD638

Mpa

6

Surrender 3

ASTMD638

Mpa

6

Surrender 5

ASTMD638

%

4

--

ASTMD152515

°C

9

--

ISO306/B50

°C

9

--

ISO306/B120

°C

1

0.45MPa, unannealed, 6.40mm

ASTMD648

°C

9

1.8MPa, unannealed, 3.20mm

ASTMD648

°C

8

1.8MPa, unannealed, 6.40mm

ASTMD648

°C

8

1.8MPa, unannealed, 64.0mm span 14

ISO75-2/Af

°C

8

Linear coefficient of thermal expansion

MD:-40到40°C

ASTME831,ISO11359-2

cm/cm/°C

5

Linear coefficient of thermal expansion

TD:-40到40°C

ASTME831,ISO11359-2

cm/cm/°C

6

Surface resistivity

ASTMD257

ohms

3

Volume resistivity

ASTMD257

ohms·cm

2

23°C

ASTMD256

J/m

2

23°C13

ISO180/1A

kJ/m²

1

-30°C

ASTMD256

J/m

8

-30°C12

ISO180/1A

kJ/m²

5

Impact strength of simply supported beam gap 11

-30°C

ISO179/1eA

kJ/m²

5

Impact strength of simply supported beam gap 11

23°C

ISO179/1eA

kJ/m²

1

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

5

Hot filament ignition temperature

1.00mm

IEC60695-2-13

°C

8

Hot filament ignition temperature

3.00mm

IEC60695-2-13

°C

8

Burning wire flammability index

0.800mm

IEC60695-2-12

°C

9