Melt flow rate

250°C/5.0 kg

ASTM D1238

g/10 min

4

Molten Volume Flow Rate (MVR)

250°C/5.0 kg

ISO 1133

cm3/10min

2

Shrinkage rate

横向流动 : 3.20 mm

内部方法

%

0

Shrinkage rate

横向流动  2

内部方法

%

0

Shrinkage rate

流动 : 3.20 mm

内部方法

%

0

Shrinkage rate

流动  2

内部方法

%

0

Specific volume

ASTM D792

cm³/g

0

Water absorption rate

平衡, 23°C, 50% RH

ISO 62

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

0

Tensile strength

断裂

ISO 527-2/5

Mpa

1

Tensile strength

断裂 4

ASTM D638

Mpa

1

Tensile strength

屈服

ISO 527-2/5

Mpa

1

Tensile strength

屈服 4

ASTM D638

Mpa

1

Tensile modulus

--

ISO 527-2/1

Mpa

1

Tensile modulus

-- 3

ASTM D638

Mpa

1

elongation

断裂

ISO 527-2/5

%

1

elongation

断裂 4

ASTM D638

%

2

elongation

屈服

ISO 527-2/5

%

1

elongation

屈服 4

ASTM D638

%

2

Taber abraser

1000 Cycles, 1000 g, CS-17 转轮

内部方法

mg

2

Bending modulus

-- 6

ISO 178

Mpa

9

Bending modulus

50.0 mm 跨距 5

ASTM D790

Mpa

9

Bending stress

--

ISO 178

Mpa

1

Bending stress

断裂, 50.0 mm 跨距 5

ASTM D790

Mpa

1

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

thermal conductivity

ISO 8302

W/m/K

0

Vicat softening temperature

--

ASTM D152510, ISO 306/B50, ISO 306/B120

°C

2

Vicat softening temperature

--

ISO 306/A50

°C

2

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ASTM E831, ISO 11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

流动 : 23 到 80°C

ISO 11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

8

Linear coefficient of thermal expansion

横向 : -40°C

ISO 11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

横向 : 23 到 80°C

ISO 11359-2

cm/cm/°C

1

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

2

Thermal deformation temperature under load

0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9

ISO 75-2/Be

°C

2

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

2

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9

ISO 75-2/Ae

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8

ISO 75-2/Af

°C

2

Surface resistivity

IEC 60093

ohms

>

Dielectric strength

1.60 mm, 在油中

IEC 60243-1

KV/mm

2

Dielectric strength

3.20 mm, 在油中

IEC 60243-1

KV/mm

1

Dielectric strength

1.60 mm, in Oil

ASTM D149

KV/mm

2

Dielectric strength

3.20 mm, in Air

ASTM D149

KV/mm

1

Dielectric strength

0.800 mm, 在油中

IEC 60243-1

KV/mm

2

Leakage Trace Index

--

IEC 60112

V

1

Leakage Trace Index

解决方案 B

IEC 60112

V

1

Volume resistivity

ASTM D257, IEC 60093

ohms·cm

>

Impact strength of simply supported beam gap 7

-30°C

ISO 179/1eA

kJ/m²

6

Impact strength of simply supported beam gap 7

23°C

ISO 179/1eA

kJ/m²

7

The impact strength of a simply supported beam without a notch is 7

-30°C

ISO 179/1eU

kJ/m²

5

The impact strength of a simply supported beam without a notch is 7

23°C

ISO 179/1eU

kJ/m²

5

Non notched cantilever beam impact

23°C

ASTM D4812

J/m

6

Non notched cantilever beam impact

-30°C 8

ISO 180/1U

kJ/m²

4

Non notched cantilever beam impact

23°C 8

ISO 180/1U

kJ/m²

4

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

5

Ball pressure hardness

H 358/30

ISO 2039-1

Mpa

1

Extreme Oxygen Index

ISO 4589-2

%

3

Burning wire flammability index

1.0 mm

IEC 60695-2-12

°C

9