Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS AG15E1-H FCFC TAIWAN
TAIRILAC®
calculator、Clock housing、Phone、suitcase、Toy、Sound enclosure
High gloss、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/FCFC TAIWAN/AG15E1-H
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
1
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
200°C/5.0kg
ISO1133
g/10min
1
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
2
Shrinkage rate
MD
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/FCFC TAIWAN/AG15E1-H
Tensile strength
23°C
ASTMD638
Mpa
5
Tensile stress
屈服,23°C
ISO527-2
Mpa
5
Bending modulus
23°C
ASTMD790
Mpa
2
Bending modulus
23°C
ISO178
Mpa
2
bending strength
23°C
ASTMD790
Mpa
8
Bending stress
23°C
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
ABS/FCFC TAIWAN/AG15E1-H
Hot deformation temperature
1.8MPa,未退火,12.7mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,12.7mm
ISO75-2/A
°C
8
Hot deformation temperature 2
1.8MPa,Annealed
ASTMD648
°C
9
Hot deformation temperature 2
1.8MPa,退火
ISO75-2/A
°C
9
Vicat softening temperature
ASTMD15253
°C
1
Vicat softening temperature
ISO306/A
°C
1