Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC URZ2501 IDEMITSU JAPAN
TARFLON™
Electrical field、Electronic field、Automotive sector、Lighting fixtures
Flame retardant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/URZ2501
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
1
physical property
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/URZ2501
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
1
Shrinkage rate
TD:2.00mm
内部方法
%
0
Shrinkage rate
MD:2.00mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/URZ2501
Nominal tensile fracture strain
ISO527-2
%
7
elongation at break
ASTM D638/ISO 527
%
t
Tensile modulus of elasticity
ISO 527-1
Mpa
2
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Tensile yield stress
ISO 527-1
Mpa
6
Tensile stress
屈服
ISO527-2
Mpa
5
Gap impact strength
ISO 176
k/Jm2
4
elongation
断裂
ISO 527-1
%
6
Flexural modulus of elasticity
ISO 178
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
ISO 178
Mpa
9
Bending stress
ISO178
Mpa
8
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
Thermal performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/URZ2501
RTIElec
UL746
°C
8
Evolution Calendar intelligent importer
UL746
°C
8
RTIStr
UL746
°C
8
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa
ISO 75-1-2
°C
1
Hot deformation temperature
0.46MPa
ISO 75-1-2
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
6
optical performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/URZ2501
transmissivity
1000µm
ISO13468-1
%
0
Other performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/URZ2501
MVR
ISO 1133
cm3/10min
1