Melt volume flow rate

265°C/5.0kg

ISO1133

cm3/10min

1

Melt mass flow rate

266°C/5.0kg

ASTMD1238

g/10min

2

Shrinkage rate

MD：3.20mm

内部方法

%

1

Shrinkage rate

TD：3.20mm

内部方法

%

1

Specific volume

ASTMD792

cm³/g

0

Water absorption rate

饱和,23°C

ISO62

%

0

Tensile strength 3

屈服

ASTMD638

Mpa

4

Tensile strength 3

断裂

ASTMD638

Mpa

3

Tensile modulus

ISO527-2/1

Mpa

1

Tensile modulus 2

ASTMD638

Mpa

1

Tensile strain

屈服

ISO527-2/50

%

3

Tensile strain

断裂

ISO527-2/50

%

1

Tensile stress

断裂

ISO527-2/50

Mpa

3

Tensile stress

屈服

ISO527-2/50

Mpa

4

Elongation rate 3

屈服

ASTMD638

%

4

Elongation rate 4

断裂

ASTMD638

%

1

Bending modulus 4

50.0mm跨距

ASTMD790

Mpa

1

Bending modulus 5

ISO178

Mpa

1

Bending strength 4

屈服,50.0mm跨距

ASTMD790

Mpa

6

Bending strength 5,6

ISO178

Mpa

6

RTIElec

UL746

°C

7

Evolution Calendar intelligent importer

UL746

°C

7

RTIStr

UL746

°C

7

Hot deformation temperature

0.45MPa,未退火,6.40mm

ASTMD648

°C

9

Hot deformation temperature

1.8MPa,未退火,6.40mm

ASTMD648

°C

6

Hot deformation temperature 9

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

5

Vicat softening temperature

ASTMD152510

°C

1

Vicat softening temperature

--

ISO306/B50

°C

1

Vicat softening temperature

--

ISO306/B120

°C

1

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

9

Linear coefficient of thermal expansion

MD：-40到40°C

ISO11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40到40°C

ISO11359-2

cm/cm/°C

1

Impact strength of simply supported beam gap 7

23°C

ISO179/1eA

kJ/m²

7

Suspended wall beam gap impact strength 8

-30°C

ISO180/1A

kJ/m²

5

Suspended wall beam gap impact strength 8

23°C

ISO180/1A

kJ/m²

5

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

5