Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C1200HF GY61117 SABIC INNOVATIVE US
CYCOLAC™
Electrical field、Electronic field、Automotive interior parts
High impact resistance、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/C1200HF GY61117
Melt flow rate
260°C/5.0 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
265°C/5.0 kg
ISO 1133
cm3/10min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/C1200HF GY61117
Tensile strength
屈服 3
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
5
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 3
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
--
ISO 178
Mpa
2
Bending stress
--
ISO 178
Mpa
8
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/C1200HF GY61117
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
8
Vicat softening temperature
ISO 306/B50
°C
1
Linear coefficient of thermal expansion - flow
-40 到 40°C
ASTM E831
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6
ISO 75-2/Bf
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6
ISO 75-2/Af
°C
1
Impact performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/C1200HF GY61117
Dart impact equipped with measuring instruments
-30°C, Total Energy
ASTM D3763
J
5
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
5