Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 WRF403 NC010 DUPONT USA
Zytel®
Automotive Applications、sporting goods
Glass fiber reinforced、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA66/DUPONT USA/WRF403 NC010
Molding shrinkage rate
ASTM D955
%
0
physical property
Test Condition
Test Method
Unit
PA66/DUPONT USA/WRF403 NC010
Shrinkage rate
(Dry)，（Flow）
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/WRF403 NC010
Charpy notch impact strength
(Dry)
ISO 179
kJ/m²
1
Fracture point tensile strain
(Dry)
ISO 527-1, -2
%
2
Fracture point tensile stress
(Dry)
ISO 527-1, -2
Mpa
1
elongation at break
ASTM D638/ISO 527
%
2
Non notched impact strength
(Dry)
ISO 180
kJ/m²
7
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile modulus
(Dry)
ISO 527-1, -2
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Gap impact strength
(Dry)
ISO 180
kJ/m²
1
Bending modulus
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
9
Bending modulus
(Dry)
ISO 178
Mpa
9
bending strength
(Dry)
ISO 178
Mpa
2
bending strength
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
2
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
8
Thermal performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/WRF403 NC010
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature/A
1.80 Mpa，未退火(Dry)
ISO 75A-1, -2
°C
2
Melting temperature
(Dry)
ISO 3146
°C
2