Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AES SE20 UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Dissolved volume flow rate
220℃/2.16 kg
ISO 1133
cm3/10min
1
Melt flow index
220℃/10Kg
ISO1133
cm3/10min
1
Shrinkage rate
MD2.0mm
ISO294-4
%
0
Shrinkage rate
MD，23℃
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
5
Charpy Notched Impact Strength
-30℃
ISO 179
kJ/m²
5
Tensile modulus
23℃
ISO 527-2
Mpa
2
Tensile modulus
23°C
ISO527-2
Mpa
2
tensile strength
23°C
ISO527-2
Mpa
4
Tensile stress
23℃
ISO 527-2
Mpa
4
Rockwell hardness
23℃
ISO 2039-2
R 计秤
1
Bending modulus
23°C
ISO178
Mpa
2
Bending modulus
23℃
ISO 178
Mpa
2
bending strength
23℃
ISO 178
Mpa
7
bending strength
23°C
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Hot deformation temperature
1.80MPa，未退火
ISO 75-2/Af
°C
8
Hot deformation temperature
1.80MPa退火
ISO75-2/Af
°C
8
Coefficient of linear expansion
MD
ISO11359-2
cm/cm/°C
9
Linear expansion coefficient
流动
ISO 11359-2
cm/cm/℃
0
Electrical performance
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Insulation strength
IEC60243-1
KV/mm
3
Volume resistance
IEC60093
Ω.cm
1
hardness
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Rockwell hardness
ISO2039-2
R
1
flammability
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Fire rating
UL-94
HB
1
Fire rating
UL-94
HB
3