Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 HTNFR53G50NHLWSF DUPONT USA
Zytel®
Food containers
Flame retardant、Thermal stability、High temperature resistan、Glass fiber reinforced、Filler: Glass fiber reinf、50% filler by weight、Filler, mineral filler, 1
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
density
ISO1183
g/cm³
1
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
2
Shrinkage rate
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
Tensile modulus
ISO527-2
Mpa
1
Tensile strain
屈服
ISO527-2/1
%
5
Tensile stress
屈服
ISO527-2/50
Mpa
2
Bending modulus
ISO178
Mpa
1
Bending stress
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
5
Vicat softening temperature
--
ISO306/A
°C
1
Vicat softening temperature
--
ISO306/B
°C
5
Impact performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
Charpy Notched Impact Strength
-20°C
ISO179/1eA
kJ/m²
3
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam without notch
-20°C
ISO179/1eU
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
1
Unscented Izod impact strength
-20°C
ISO180/1U
kJ/m²
3
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
1
Impact strength of cantilever beam gap
-20°C
ISO180/1A
kJ/m²
3
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
hardness
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
Ball pressure hardness
H358/30
ISO2039-1
Mpa
4
flammability
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
Fogging-
100°C
DIN75201
mg
<
Supplementary Information
Test Condition
Test Method
Unit
PA66/DUPONT USA/HTNFR53G50NHLWSF
Emission
VDA277
µgC/g
<