Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI EX07305-WH8E546 SABIC INNOVATIVE SHANGHAI
ULTEM™
Electrical and Electronic、Automotive components
Glass fiber reinforced、lubrication、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/EX07305-WH8E546
Shrinkage rate
MD
内部方法
%
0
Shrinkage rate
TD
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/EX07305-WH8E546
--
ISO527-2/1
Mpa
8
--1
ASTMD638
Mpa
8
--5
ISO178
Mpa
7
50.0mm span 4
ASTMD790
Mpa
6
crack
ISO527-2/5
%
1
crack
ISO527-2/5
Mpa
1
Fracture 2
ASTMD638
Mpa
1
Fracture 3
ASTMD638
%
3
Wear factor - Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
1
Bending strength 6
屈服,50.0mm跨距
ASTMD790
Mpa
2
Bending strength 6
断裂,50.0mm跨距
ASTMD790
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/EX07305-WH8E546
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
2
1.8MPa, unannealed, 64.0mm span 9
ISO75-2/Af
°C
2
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/EX07305-WH8E546
Surface resistivity
ASTMD257
ohms
2
Dielectric strength
1.60mm,inOil
ASTMD149
KV/mm
3
Volume resistivity
ASTMD257
ohms·cm
7
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/EX07305-WH8E546
23°C
ASTMD4812
J/m
3
23°C
ASTMD256
J/m
6
23°C7
ISO180/1A
kJ/m²
7
23°C8
ISO180/1U
kJ/m²
2