PPS OX11315 BK SABIC INNOVATIVE US
LNP™ KONDUIT™
Automotive Applications
Carbon fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OX11315 BK
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
<
Mechanical performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OX11315 BK
Tensile strength 3
断裂
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/1
Mpa
1
Tensile modulus 2
ASTMD638
Mpa
3
Tensile strain
断裂
ISO527-2/5
%
0
Tensile stress
断裂
ISO527-2/5
Mpa
5
Elongation rate 4
断裂
ASTMD638
%
0
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 5
断裂,50.0mm跨距
ASTMD790
Mpa
8
Bending stress
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OX11315 BK
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
specific heat
ASTMC351
J/kg/°C
1
thermal conductivity
--8
ASTM D790/ISO 178
W/m/K
3
thermal conductivity
--9
ASTM D790/ISO 178
W/m/K
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature 7
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
2
Hot deformation temperature 7
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
2
Electrical performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OX11315 BK
Surface resistivity
ASTMD257
ohms
2
Impact performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OX11315 BK
Multi axis Instrumented Impact Energy
ISO6603-2
J
1
Unscented Izod Impact Strength 5
23°C
ISO180/1U
kJ/m²
3
Suspended wall beam notch impact strength 6
23°C
ISO180/1A
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
5