PA66 RL-4020 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical、Automotive components、Lighting fixtures
High temperature resistan、resist fatigue
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RL-4020
Shrinkage rate
MD:24小时
ASTMD955
%
2
Shrinkage rate
TD:24小时
ASTMD955
%
2
Shrinkage rate
TD:24小时
ISO294-4
%
2
Shrinkage rate
MD:24小时
ISO294-4
%
2
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RL-4020
Tensile strength
屈服
ASTMD638
Mpa
7
Tensile strength
屈服
ISO527-2
Mpa
7
Tensile strength
断裂
ASTMD638
Mpa
7
Tensile strength
断裂
ISO527-2
Mpa
7
Tensile modulus
--2
ASTMD638
Mpa
3
Tensile modulus
--
ISO527-2/1
Mpa
3
Wear factor - Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
4
elongation
屈服
ASTMD638
%
1
elongation
屈服
ISO527-2
%
1
elongation
断裂
ASTMD638
%
1
elongation
断裂
ISO527-2
%
1
Bending modulus
--
ASTMD790
Mpa
3
Bending modulus
--
ISO178
Mpa
2
bending strength
--
ASTMD790
Mpa
1
bending strength
--
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RL-4020
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距4
ISO75-2/Af
°C
7
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
8
Impact performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RL-4020
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
9
Cantilever beam without notch impact strength
23°C3
ISO180/1U
kJ/m²
5
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
3
Dart impact equipped with measuring instruments
--
ISO6603-2
J
4