Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 1130A64 JAPAN POLYPLASTIC
DURAFIDE®
Fiber grade
enhance、Flame retardant、High mobility、standard、High temperature resistan、Low flash
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
Water absorption rate
(23°C,24hr)
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
elongation at break
23°C
ISO527-2
%
1
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
7
tensile strength
23°C
ISO527-2
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending modulus
23°C
ISO178
Mpa
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
23°C
ISO178
Mpa
2
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
Hot deformation temperature
1.80MPa退火
ISO75-2/Af
°C
2
Coefficient of linear expansion
MD
ISO11359-2
cm/cm/°C
2
Coefficient of linear expansion
TD
ISO11359-2
cm/cm/°C
4
Electrical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
Dissipation factor
23°C
IEC60250
1kHz
1
Dissipation factor
23°C
IEC60250
1MHz
2
Dissipation factor
耐电弧性
IEC61621
S
1
Dissipation factor
相对漏电起痕指数
IEC60112
V
1
Dielectric constant
23°C
IEC60250
1kHz
4
Dielectric constant
23°C
IEC60250
1MHz
4
Insulation strength
3mm
IEC60243-1
KV/mm
1
Volume resistance
IEC60093
Ω.cm
8
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
8
hardness
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
Rockwell hardness
ISO2039-2
M（Scale）
1
flammability
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1130A64
Fire rating
UL-94
V-0
0
Fire rating
UL-94
V-0
0
Fire rating
UL-94
V-0
1
Fire rating
UL-94
V-0
3