Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO SE1X-701 SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Electronic and electrical
Flame retardant、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/SE1X-701
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 2
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/SE1X-701
Tensile strength 3
屈服
ASTM D638
Mpa
6
Tensile strength 3
断裂
ASTM D638
Mpa
5
Elongation rate 3
屈服
ASTM D638
%
8
Elongation rate 3
断裂
ASTM D638
%
2
Bending modulus
100 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 100 mm 跨距
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/SE1X-701
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/SE1X-701
Surface resistivity
ASTM D257
ohms
>
Dielectric strength
3.20 mm, in Oil
ASTM D149
KV/mm
1
Volume resistivity
ASTM D257
ohms·cm
2
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/SE1X-701
Dart impact equipped with measuring instruments
-30°C, Energy at Peak
ASTM D3763
J
3
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
5