Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT X4850-78211 SABIC INNOVATIVE US
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X4850-78211
Melt volume flow rate
265°C/5.0kg
ISO1133
cm3/10min
4
Melt mass flow rate
266°C/5.0kg
ASTMD1238
g/10min
4
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X4850-78211
FlexuralStrength5
Yield,50.0mmSpan
ASTMD790
Mpa
9
Tensile strength
屈服
ASTMD638
Mpa
5
Tensile strength
屈服
ASTMD638
Mpa
6
Tensile strength
断裂3
ASTMD638
Mpa
6
Tensile strength
断裂4
ASTMD638
Mpa
5
Tensile modulus
ISO527-2/1
Mpa
3
Tensile modulus 2
ASTMD638
Mpa
4
Tensile strain
断裂
ISO527-2/5
%
8
Tensile strain
断裂
ISO527-2/50
%
3
Tensile strain
屈服
ISO527-2/5
%
3
Tensile strain
屈服
ISO527-2/50
%
3
Tensile stress
断裂
ISO527-2/50
Mpa
4
Tensile stress
断裂
ISO527-2/5
Mpa
5
Tensile stress
屈服
ISO527-2/5
Mpa
5
Tensile stress
屈服
ISO527-2/50
Mpa
6
elongation
屈服
ASTMD638
%
3
elongation
屈服
ASTMD638
%
3
elongation
断裂3
ASTMD638
%
1
elongation
断裂4
ASTMD638
%
1
Taber abraser
1000Cycles,1000g,CS-17转轮
内部方法
mg
3
Bending modulus 5
50.0mmSpan
ASTMD790
Mpa
3
Bending modulus 6
ISO178
Mpa
3
Bending strength 6,7
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X4850-78211
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
9
Hot deformation temperature 10
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Vicat softening temperature
ASTMD152511
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
MD：-30到80°C
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-30to80°C
ISO11359-2
cm/cm/°C
8
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X4850-78211
Multi axis Instrumented Impact Energy
ISO6603-2
J
1
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
2
Suspended wall beam gap impact strength 9
-30°C
ISO180/1A
kJ/m²
7
Suspended wall beam gap impact strength 9
0°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength 9
23°C
ISO180/1A
kJ/m²
2
Dart impact equipped with measuring instruments
-20°C,TotalEnergy
ASTMD3763
J
6
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6
hardness
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X4850-78211
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1