Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EVOH F101B NIPPON GOHSEI
--
--
copolymer、Lubricity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Ethylene
内部方法
mol%
3
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
1
Melt mass flow rate
210°C/2.16kg
ISO1133
g/10min
3
Mechanical performance
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Tensile modulus
ISO527-2
Mpa
2
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
3
Bending modulus
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Glass transition temperature
ISO11357-2
°C
6
Crystallization peak temperature
ISO11357-3
°C
1
Melting temperature
ISO11357-3
°C
1
Vicat softening temperature
ISO306
°C
1
film
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Water vapor permeability 3
ASTME96
g·mm/m²/atm/24hr
1
Oxygen permeability rate 2
20°C,100%RH
ISO14663-2
cm³·mm/m²/atm/24hr
0
Oxygen permeability rate 2
20°C,35%RH
ISO14663-2
cm³·mm/m²/atm/24hr
6
Oxygen permeability rate 2
20°C,65%RH
ISO14663-2
cm³·mm/m²/atm/24hr
8
Oxygen permeability rate 2
20°C,85%RH
ISO14663-2
cm³·mm/m²/atm/24hr
0
Oxygen permeability rate 2
20°C,90%RH
ISO14663-2
cm³·mm/m²/atm/24hr
0
Oxygen permeability rate 2
20°C,0%RH
ISO14663-2
cm³·mm/m²/atm/24hr
4
Impact performance
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Unscented Izod impact strength
ISO180
kJ/m²
2